Título: Síntese e caracterização de vanadato de ítrio contendo íons Nd3+ a partir do processo Sol Gel
Título(s) alternativo(s): Synthesis and characterization of yttrium vanadate containing ions Nd3 + from the Sol Gel process
Autor(es): Tanaka, Julio Tadashi
Primeiro Orientador: Rocha, Lucas Afonso
metadata.dc.contributor.referee1: Marçal, Alex Lemes
metadata.dc.contributor.referee2: Nassar, Eduardo José
metadata.dc.contributor.referee3: Castro, Gustavo Rocha de
metadata.dc.contributor.referee4: Silva, Liziane Marçal da
Resumo: Realizou-se neste trabalho, uma análise de matrizes inorgânicas de vanadato de ítrio (YVO4) preparadas pela adaptação do processo Sol Gel rota não hidrolítica incorporada com diferentes concentrações de íons Nd3+, e submetidas a tratamento térmico nas temperaturas de 600, 800 e 1.000 °C. As amostras foram caracterizadas por Difratometria de Raios X, Espectroscopia Vibracional RAMAN e Espectroscopia de Fotoluminescência. O trabalho foi dividido em duas etapas com objetivos distintos. Na primeira etapa, o foco esteve na otimização da concentração ideal para a formação da fase pura de YVO4, também denominada matriz hospedeira. Para isso, várias amostras foram sintetizadas contendo diferentes concentrações de ítrio e vanádio, mantendo-se a concentração de neodímio em 1% em mol em relação ao vanádio. A segunda etapa consistiu na incorporação de diferentes concentrações de íons Nd3+ (1% - 20% em mol em relação ao vanádio) com o objetivo de se avaliar a influência deste íon tanto nas propriedades estruturais da matriz quanto em sua fotoluminescência. Os resultados sugerem que a amostra contendo a concentração molar vanádio: ítrio: neodímio (59%: 40%: 1%) apresentou a fase pura do YVO4. Na fotoluminescência foi possível observar que apesar de aumentar a concentração do íon Nd3+ houve uma diminuição nas propriedades luminescentes da matriz e através do difratograma de raios X observou-se que após os tratamentos térmicos a estrutura cristalina do YVO4 não foi alterada significativamente, porém quando tratado a 600ºC possui características do oxido de vanádio o qual se acomodou na matriz após o aumento da temperatura de tratamento
Abstract: In this work, an analysis of inorganic yttrium vanadate (YVO4) matrices prepared by the adaptation of the non-hydrolytic route Sol Gel process incorporated with different concentrations of Nd3+ ions was carried out and subjected to thermal treatment at temperatures of 600, 800 and 1000°C. The samples were characterized by X-ray diffractometry, RAMAN Vibrational Spectroscopy and Photoluminescence Spectroscopy. The work was divided into two stages with different objectives. In the first step, the focus was on optimizing the ideal concentration for the formation of the pure YVO4 phase, also called the host matrix. For this, several samples were synthesized containing different concentrations of yttrium and vanadium, maintaining the concentration of neodymium in 1% in mol in relation to vanadium. The second step consisted in the incorporation of different concentrations of Nd3+ ions (1% - 20% in mol, in relation to vanadium) in order to evaluate the influence of this ion in both the structural properties of the matrix and its photoluminescence. The results suggest that the sample containing the vanadium: yttrium: neodymium (59%: 40%: 1%) molar concentration showed the pure YVO4 phase. In the photoluminescence it was possible to observe that in spite of increasing the concentration of the Nd3+ ion there was a decrease in the luminescent properties of the matrix and through the X-ray diffraction it was observed that after the thermal treatments the crystalline structure of YVO4 was not significantly altered, however when treated at 600°C has characteristics of the vanadium oxide which has settled in the matrix after the increase of the treatment temperature.
Palavras-chave: Terras raras
Matriz hospedeira
YVO4
Fase pura
Fotoluminescência
CNPq: CNPQ::CIENCIAS EXATAS E DA TERRA
Idioma: por
País: Brasil
Editor: Universidade de Franca
Sigla da Instituição: UNIFRAN
Departamento: Pós-Graduação
Programa: Programa de Doutorado Ciências
Citação: TANAKA, Julio Tadashi. Síntese e caracterização de vanadato de ítrio contendo íons Nd³+ a partir do processo Sol Gel. Franca, SP, 2017. 93 f. Tese (Doutorado) - Universidade de Franca. 2017.
Tipo de Acesso: Acesso Aberto
URI: https://repositorio.cruzeirodosul.edu.br/handle/123456789/394
Data do documento: 10-Fev-2017
Aparece nas coleções:Doutorado em Ciências

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Julio Tadashi Tanaka.pdf3.12 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.